Mendagaliyev, R., Klimova-Korsmik, O.G., Ivanov, S.Y., Babkin, K.D., Vildanov, A.M.
(2021) Journal of Physics: Conference Series, 2077 (1), статья № 012012.
https://doi.org/10.1088/1742-6596/2077/1/012012
КРАТКОЕ ОПИСАНИЕ: The formation of microstructure features of cold-resistant bainite-martensite steel 09CrNi2MoCu has been investigated. Thermal cycles during direct laser deposition were studied. The thermal cycles at different points of the deposited samples were investigated. The thermal cycles and CCT diagrams on microstructure formation and mechanical properties have been analyzed. The numerical calculation of the three-dimensional thermal conductivity problem by the finite element method is carried out. The received data of experimentally measured thermal cycles and the calculated data have shown good coincidence of temperature values. On the basis of the obtained data the calculated dependence of inter-layer temperature at depositing the sample with and without a pause is given. The microstructure and mechanical properties of the samples in the initial state and after heat treatment have been studied and compared with traditional hot rolling. The microstructure features at different pauses between passes in different parts of the obtained samples were revealed. The effect on static tensile and impact toughness at -40°C in the bred and heat-treated state was investigated.
https://iopscience.iop.org/article/10.1088/1742-6596/2077/1/012012
(2021) Journal of Physics: Conference Series, 2077 (1), статья № 012012.
https://doi.org/10.1088/1742-6596/2077/1/012012
КРАТКОЕ ОПИСАНИЕ: The formation of microstructure features of cold-resistant bainite-martensite steel 09CrNi2MoCu has been investigated. Thermal cycles during direct laser deposition were studied. The thermal cycles at different points of the deposited samples were investigated. The thermal cycles and CCT diagrams on microstructure formation and mechanical properties have been analyzed. The numerical calculation of the three-dimensional thermal conductivity problem by the finite element method is carried out. The received data of experimentally measured thermal cycles and the calculated data have shown good coincidence of temperature values. On the basis of the obtained data the calculated dependence of inter-layer temperature at depositing the sample with and without a pause is given. The microstructure and mechanical properties of the samples in the initial state and after heat treatment have been studied and compared with traditional hot rolling. The microstructure features at different pauses between passes in different parts of the obtained samples were revealed. The effect on static tensile and impact toughness at -40°C in the bred and heat-treated state was investigated.
https://iopscience.iop.org/article/10.1088/1742-6596/2077/1/012012