Mendagaliyev, R., Turichin, G.A., Klimova-Korsmik, O.G., Zotov, O.G., Eremeev, A.D.
(2019) Procedia Manufacturing, 36, pp. 249-255.
https://doi.org/10.1016/j.promfg.2019.08.032
КРАТКОЕ ОПИСАНИЕ: The article presents the study of the direct laser deposition (DLD) process of cold-resistant steel 09CrNi2MoCu (F620W). As a result, many bainite transformation products are produced. The formation of a bainitic structure in the process of deposition is still little studied; in the process of the growth of the deposited wall, the microstructure undergoes a phase transformation. The work details the equipment for direct laser deposition, describes the main technological parameters of the regime, and studies the surface of the steel powder. Mechanical tests for impact toughness were carried out at a temperature of .40°N, with different laser emission powers. The results are given using the initial powder, as well as used powder with a different mixing ratio, and the results are analyzed. As a result of the study, it was established that the fractional composition of the F620W alloy powder has a significant effect on the mechanical characteristics of samples obtained by direct laser deposition. The effect of recycled powder on the mechanical properties of the samples obtained is given.
https://www.sciencedirect.com/science/article/pii/S2351978919310406?via%3Dihub
(2019) Procedia Manufacturing, 36, pp. 249-255.
https://doi.org/10.1016/j.promfg.2019.08.032
КРАТКОЕ ОПИСАНИЕ: The article presents the study of the direct laser deposition (DLD) process of cold-resistant steel 09CrNi2MoCu (F620W). As a result, many bainite transformation products are produced. The formation of a bainitic structure in the process of deposition is still little studied; in the process of the growth of the deposited wall, the microstructure undergoes a phase transformation. The work details the equipment for direct laser deposition, describes the main technological parameters of the regime, and studies the surface of the steel powder. Mechanical tests for impact toughness were carried out at a temperature of .40°N, with different laser emission powers. The results are given using the initial powder, as well as used powder with a different mixing ratio, and the results are analyzed. As a result of the study, it was established that the fractional composition of the F620W alloy powder has a significant effect on the mechanical characteristics of samples obtained by direct laser deposition. The effect of recycled powder on the mechanical properties of the samples obtained is given.
https://www.sciencedirect.com/science/article/pii/S2351978919310406?via%3Dihub